Synthesis of a Fe3O4-rGO-ZnO-catalyzed photo-Fenton system with enhanced photocatalytic performance

In this work, we designed a magnetically-separable Fe₃O₄-rGO-ZnO ternary catalyst, ZnO anchored on the surface of reduced graphene oxide (rGO)-wrapped Fe₃O₄ magnetic nanoparticles, where rGO, as an effective interlayer, can enhance the synergistic effect between ZnO and Fe₃O₄. The effects of three operational parameters, namely irradiation time, hydrogen peroxide dosage, and the catalyst dosage, on the photo-Fenton degradation of methylene blue and methyl orange were investigated. The results showed that the Fe₃O₄-rGO-ZnO had great potential for the destruction of organic compounds from wastewater using the Fenton chemical oxidation method at neutral pH. Repeatability of the photocatalytic activity after 5 cycles showed only a tiny drop in the catalytic efficiency.     

Microstructure and electromagnetic properties of LiFe5O8 ferrite ceramics prepared from wet- and dry-milled powders

The effect of dry and wet ball milling of LiFe₅O₈ ferrite powder on the microstructure and electromagnetic properties of ferrite ceramics was studied using XRD analysis, scanning electron microscopy, dilatometry, thermogravimetry, calorimetry, and measurement of specific magnetization and electrical resistance. The sintering temperature was 1050 °C; the sintering time was 2 h. It was found that ferrite fabricated from dry-milled powder exhibits an ordered α-LiFe₅O₈ phase with bulk density of 91%. Its saturation magnetization and Curie temperature are 55 emu/g and 628°С, respectively. Specific electrical resistance is 4?10⁶ Ω cm. Wet milling in isopropyl alcohol causes formation of a disordered β-LiFe₅O₈ phase. Ceramics produced by this method shows higher bulk density (97%) and low porosity, and an order of magnitude lower resistivity. Its saturation magnetization and Curie temperature are 51 emu/g and 607°С, respectively.     

Effect of atmosphere control on magnetic properties of CaO-Al2O3-SiO2-Fe3O4 glass ceramics

The influences of atmosphere during processes of melting and heat treatment, heat treatment temperature, Fe₃O₄ content and basicity on the magnetic properties of magnetite-based glass ceramics were investigated. For sample containing 20 % Fe₃O₄ melted in different atmospheres, the highest saturation magnetisation was realized in 20vol% air + 80 vol% Ar, due to the fact that ratio of Fe³⁺ to Fe²⁺ in melt obtained in this atmosphere was close to 2. However, it was found that the coercivity of glass ceramics was not affected by the melting atmosphere. A high sintering temperature led to the decrease of saturation magnetisation and the increase of coercivity. As increasing Fe₃O₄ content, the main crystal phase transformed from CaSiO₃ to CaFe_0.6Al_1.3Si_1.08O₆ and finally to magnetite phase, accompanied by the increase of saturation magnetisation and coercivity. In addition, the increase of basicity caused the decrease of saturation magnetisation and the increase of coercivity.     

水力空化改质对重质原油沥青质及性质的影响

利用水力空化过程产生局部的高温、高压、高射流以及强大的剪切力等极端化学物理条件改质处理沙特重质原油，试验结果表明：沙特重质原油经过水力空化改质后粘度由13.61降低至7.22mm2/s，残碳由7.16%降低至6.48%，实沸点蒸馏后减压渣油降低1个百分点。进一步采用APPI FT-IR MS、XRD、FT-IR、SEM和粒度分布等技术研究了水力空化改质对沙重原油分子组成，沥青质团聚体微晶结构、沥青质胶束粒径分布、沥青质官能团、沥青质形貌等方面的影响，从分子角度阐述空化改质重油的机理。研究结果表明：水力空化改质后沙重原油分子量分布、芳烃类化合物缔合作用变小；沥青质对低DBE化合物吸附性能降低；沥青质团聚体微晶结构更加松散；沥青质胶束粒度分布降低；沥青质分子相互团聚作用力减弱。进一步考察了水力空化改质前后减压渣油延迟焦化性能，改质处理后焦炭产率降低1.85个百分点，液体收率和气体产率分别增加1.52和0.33个百分点，水力空化改质对沥青质性质、结构特点的改善能够有效的提高其加工性能。     

Synthesis and characterization of the novel nanostructured NiC carbide obtained by mechanical alloying

In the present work, a comprehensive study of mechanical alloying of Ni-carbon nanotubes (CNT) and Ni-Graphite equiatomic powder mixtures under the same technological modes has provided to reveal the features of using different types of carbon (CNT or graphite) as a charge component. The as-milled powders were characterized by scanning electron microscopy (SEM), X-ray diffraction (XRD) and magnetometric study. A novel nanoscale fcc NiC monocarbide was synthesized regardless the type of the charge used. According to the XRD study the formation of this phase takes place in two stages. A two-step carbide formation mechanism has been proposed. The associated changes in the nickel lattice, such as changes in the lattice parameter, lattice strain and residual stresses, which led to the formation of NiC monocarbide were also evaluated and discussed. Parameters of the electronic structure of NiC were calculated using the MStudio MindLab 7.0 software package with the experimental data on the crystal structure of the NiC phase obtained as input. Temperature dependencies of magnetic susceptibility of NiC synthesized have been studied up to 950 K. Carbides synthesized were found to be weak ferromagnets at the room temperature and their Curie temperature T_C ranges within 670 – 725 K. The calculated value of the magnetic moment per nickel atom (2.83μ_B) is higher than that of a bulk Ni (1.3μ_B). Likely, the observed increase of μ is caused by the presence of a certain amount of residual single-domain ferromagnetic Ni nanoparticles in the samples synthesized.     

Structure,magnetic properties and microwave absorption properties of NdFe1-xNixO3

In this paper, a high-purity NdFe_1-xNi_xO₃ perovskite-type material was prepared by a simple sol method. At the same time, adjust the substitution content of nickel to achieve the purpose of adjusting the dielectric properties and magnetic properties. According to the respective instruments, as Ni is substituted into the NdFeO₃, the crystal microstructure will change to a certain extent, and there is a certain causal relationship between the magnetic properties and the bonding. Therefore, by adding a certain amount of nickel, the dielectric properties and magnetic properties can be adjusted to a certain balance point. NdFe_1-xNi_xO₃ material has excellent microwave absorption performance. When x = 0.2, the minimum reflection loss value is ?49.32, and the corresponding impedance matching value is 1, and the effective bandwidth is 2.2 GHz when the thickness is 5.0 mm. The material that adjusts the perovskite structure by Ni element is beneficial to make the microwave absorption peak move from high frequency to low frequency, which has a wider application range and is closer to civil, commercial, military and aerospace.     

Role of exchange coupling between the hard and soft magnetic phases on the absorption of microwaves by SrFe10Al2O19/Co0.6Zn0.4Fe2O4 nanocomposite

(1-x)SrFe₁₀Al₂O₁₉/(x)Co_0.6Zn_0.4Fe₂O₄-(SFAO/CZFO) hard/soft nanocomposite ferrite materials were synthesized by ‘one-pot’ self-propagating combustion route. The co-existence of the two magnetic phases were confirmed by XRD, FESEM, EDS and VSM. The prepared nanocomposite samples were also characterized by TGA/DSC, Raman spectroscopy and VNA. Exchange coupling between the hard and the soft magnetic grains was observed by determining the switching field distribution (SFD) curve. As a result of the competing effects of exchange interaction and dipolar interaction, magnetic parameters were observed to be sensitive to the incorporation of soft magnetic phase into the nanocomposite. Results showed that with the inclusion of soft magnetic phase, exchange coupling behaviour between the hard and the soft ferrite phases had significant influence on the microwave absorption capacity of the samples. Related electromagnetic parameters and impedance matching ratio of the nanocomposite system were discussed. A minimum reflection loss of ?42.9 dB with an absorber thickness of 2.5 mm was attained by the nanocomposite (90 wt%)SrFe₁₀Al₂O₁₉/(10 wt %)Co_0.6Zn_0.4Fe₂O₄ at a matching frequency of 11.45 GHz. This assured the candidacy of SrFe₁₀Al₂O₁₉/Co_0.6Zn_0.4Fe₂O₄ nanocomposite as a promising microwave absorption material in the X-band (8–12 GHz).     

Anisotropic thermal expansion and ionic conductivity of a crystal-oriented,Mg2+-conducting NASICON-type solid electrolyte

Multivalent ion-conducting ceramics are required for the manufacture of high-safety, high-capacity rechargeable batteries. However, the low ionic conductivity of solid electrolytes and discrepancies in the thermal expansion between the battery components limit their widespread application. Furthermore, anisotropic thermal expansion in crystals during battery manufacturing and the charge-discharge cycles causes the formation of microcracks, which degrade the battery performance. The physical properties of ceramic materials with anisotropic crystal structures can be modified by varying the crystallographic orientation of their grains. In this study, a co-precipitation approach was used to synthesize an Mg²⁺-conducting (Mg_0.1Hf_0.9)_4/3.8Nb(PO₄)₃ solid electrolyte, and the grain orientation in the bulk sample was controlled using strong magnetic fields during the slip casting process. The results showed that inducing an orientation along the c-axis enhanced the apparent ionic conductivity of the bulk sample. It was also observed that (Mg_0.1Hf_0.9)_4/3.8Nb(PO₄)₃ crystal has a negative volumetric thermal expansion despite a positive linear thermal expansion along its c-axis. By adjusting the c-axis orientation of the grains, (Mg_0.1Hf_0.9)_4/3.8Nb(PO₄)₃ electrolytes with negative or positive linear thermal expansion coefficient have been produced. The findings of this study suggest that solid-electrolytes with negative, positive, or zero linear thermal expansion can be produced to create more compatible and higher-performance solid-state devices.     

Magnetic field-enhanced photocatalytic nitrogen fixation over defect-rich ferroelectric Bi2WO6

Photocatalytic N₂ fixation is a promising and sustainable manufacturing process of ammonia (NH₃); however, the NH₃ production rate by this method is very low, thus severely restricting further application of this sustainable technology. Therefore, developing an efficient photocatalyst for N₂ fixation under mild conditions is urgently required. Herein, ferroelectric Bi₂WO₆ materials with different surface oxygen defects were prepared, and the concentration of corresponding defects was controlled by adjusting the thermal reduction time. The abundant oxygen defects in Bi₂WO₆ can provide more reactive sites to promote the effective adsorption of N₂, and the photogenerated charge carrier can be efficiently separated benefiting from the internal electric field. These would weaken the N₂ triple bond and reduce the activation energy barrier for the conversion of N₂ to NH₃ under mild conditions. In the absence of sacrificial agents and cocatalysts, the optimized Bi₂WO₆ with oxygen defects shows an indigenous NH₃ yield of 132.175 μmol·g^-1·L^-1·h^-1, which is more than two times higher than that of the original Bi₂WO₆. Surprisingly, the Bi₂WO₆ with oxygen defects produced more than eight times NH₃ (471.13 μmol·g^-1·L^-1·h^-1) than that of the original Bi₂WO₆ when assisted by an external magnetic field, thus providing a new perspective for further enhancing the N₂ fixation performance.     

Novel Bi4O5Br2/MnxZn1-xFe2O4 magnetic composite with an enhanced photodegradation activity and excellent recyclability

Bi₄O₅Br₂/Mn_xZn_1-xFe₂O₄ nanocomposites with impressive photocatalytic and recyclability properties were synthesised using a microemulsion method. In addition to the photocatalytic effect, the crystal structure and morphology, photoelectrochemical characteristics, magnetic effect and photocatalytic mechanism of Bi₄O₅Br₂/Mn_xZn_1-xFe₂O₄ were also investigated. As the best sample, the removal rate of the Bi₄O₅Br₂/Mn_xZn_1-xFe₂O₄ photocatalyst with 7.5 wt% Mn_xZn_1-xFe₂O₄ to rhodamine B (RhB) reached up to 99.4% within 60 min. The enhanced photocatalyst activity was mainly attributed to the type-II heterojunction formed between Bi₄O₅Br₂ and Mn_xZn_1-xFe₂O₄, which not only optimised the energy band structure, but also led to the building of an interior electromagnetic field within the Bi₄O₅Br₂/Mn_xZn_1-xFe₂O₄ heterojunction. Meanwhile, the constantly producing and migrating h⁺ and ·O₂^? were the main active components. In particular, the results of the saturation magnetization tests and magnetic recovery experiments revealed that the magnetic composite photocatalyst can be recovered effectively. The results of the removal rate of RhB remaining at 85.2% after five uses reflected the advantages of the stability of the Bi₄O₅Br₂/Mn_xZn_1-xFe₂O₄ photocatalyst. In brief, this paper presented an original idea to develop a novel composite magnetic photocatalyst and research the enhancement mechanism of photocatalysis.